Item 　
Fire Clay bricks
Brand 　

CN-4O

CN-42

ZGN-42

GN-42

 　

N-1

N-2a

 　
Application 　

Ladle

Ladle

Blast Furnace

Blast Furnace

Blast Furnace

 　General use 　　General use  
Type 　 Arc shape Arc shape G-shape G-shape 　 　 　 　Handwork
properties 　 　 　 　 　 　 　 　 　
Al2O3，%   ≥ 40 42 42 42 41 42 38 　
Fe2O3，% ≤ 　 　 1.6 1.7 1.8 　 　 　
P2O5，% ≥ 　 　 　 　 7 　 　 　
Ref，℃ ≥ 1730 1750 1750 1750 　 1750 1730 1730
0.2Mpa RUL，℃ ≥ 1400 1430 1450 1430 1450 1400 1350 1300
PLC，% 　 1400℃，2h 1400℃，2h 1450℃，3h 1450℃，3h 1450℃，3h 1400℃，2h 1400℃，2h 1350℃，3h
0～-0.3 0～-0.3 0～-0.2 0～-0.3 -0.2～0 0.1～-0.4 0.1～-0.5 0.1～-0.5
AP，% ≤ 19 18 15 16 14 22 24 26
CCS，Mpa ≥ 34.3 39.2 58.8 49 60 29.4 24.5 14.7
Alkali Resistance% ≤ 　 　 　 　 15 　 　 　
  　 小型钢包工作衬,中型钢包永久层 　 　 　 　 　 　


Bricks for carbon bake furnace
     Item 　 common high B.D 仿FBA 仿BFD
Al2O3，%     ≥ 42 42 42 42
Fe2O3，% ≤ 　 2 1.6 1.8
Ref，℃ ≥ 1730 1750 1750 1710
PLC,%
(1400℃,2h)

(1450℃,2h)

(1350℃,2h)		 　 　 +0.1~
-0.3		 　 +0.1~
-0.3
　 　 +0.1~
-0.3		 　
+0.1~
-0.3		 　 　 　
MOR,Mpa
1200℃,300min
1350℃,300min		 ≥

≥		 　 　 10.0

4.0		 9.0

3.0
High temp.creep,%
0.2Mpa,1280℃
25h		 ≤ 　 　 0.4 0.45
liner expension rate 1000℃,% ≤ 　 　 0.65 0.6
AP，% ≤ 23 18 19 19
CCS，Mpa ≥ 29.6 39.2 29.6 39.2

Fire clay bricks for hot air furnace

Item 　 DN-1 DN-2 DN-3
Al2O3，% ≥ 38 40 42
Fe2O3，% ≤ 2 1.8 1.7
Ref，℃ ≥ 1710 1730 1750
RUL ,℃ ≥ 1350 1400 1420
CCS，
Mpa		 ≥ 25 35 40
BD,
G/cm3		 ≥ 2.0 2.1 2.2
AP，% ≤ 24 22 18
PLC,% 　 1350
℃,2h
+0.1～
-0.3		 1350
℃,2h
+0.1～
-0.3		 1350
℃,2h
+0.1～
-0.3
High temp.creep,%
(20-50h)		 　 1150℃
≤0.2		 1150℃
≤0.2		 1150℃
≤0.2
Application 　 Hot air furnace

Bricks for casting

Item 　 SN-40 KN-40 XN-40 ZN-40 JZN-40
Brick name 　 Head Nozzle Sleeve Well block Steel casting
Al2O3
，%
 ≥ 40 40 40 40 40
Ref，℃ ≥ 1710 1710 1710 1710 1710
RUL ,℃
 ≥ 1370 1370 　 　 　
PLC ,%
(1450℃
,2h)
(1350℃
,2h)		 　 　 　 　 　 　
　 　 0～
-0.3		 　 0～
-0.3
AP，% ≤ 15～23 22 15～25 23 17～25

CCS Mpa		 ≥ 　 　 　 19.6 　
Application 　 Casting